Windbond PF 101P

General Information

WINDBOND PF-101P is a Phenol Formaldehyde Resin Powder specially developed for the manufacturing of BWR and BWP grade Plywood, Block Board, Flush Door etc. It meets all the requirements for the preparation of Boiled Water Proof adhesive and used in the manufacture of exterior and marine grades Plywood. It is used in hot bonding process.

1. PHYSICAL PROPERTIES AND SPECIFICATIONS OF WINDBOND PF-101P (E1 GRADE)

PROPERTIES SPECIFIC VALUES
APPEARANCE : REDDISH-BROWN FREE FLOWING POWDER
VISCOSITY (1:1) AT 25°C : 22-45 SEC IN B4 CUP
pH OF 50% SOLUTION AT 25°C : 10.5-11.5%
GEL TIME AT 140°C : 5-6 MINUTES
WATER TOLERANCE IN 50% SOLUTION (1:1) : 1:>10.0
SOLUBILITY : EASILY SOLUBLE IN WATER
FREE FORMALDEHYDE AT 50%SOLN. : <0.4%

 

2. GLUE PREPARATION

PREPARATION OF GLUE MIX BWR Grade BWP Grade
POWDER 100 PARTS BY WT. 100 PARTS BY WT.
WATER 120 PARTS BY WT. 100 PARTS BY WT.
WHEAT FLOUR / CSP 5 TO 8 % OF TOTAL WEIGHT (POWDER + WATER) 5 TO 8 % OF TOTAL WEIGHT (POWDER + WATER)
ADDITIVE NIL NIL

 

4. REACTIVITY OF GLUE

Local conditions determine the selection of reactivity. The reactivity of the glue can be adjusted over a wide range by varying the composition and quantity of hardener.

Glue should be used within 24 hrs. of its preparation. Longer storage will increase viscosity and reduce its bonding strength. To adjust the viscosity, water and 􀀀ller quantity may be adjusted.

6. ASSEMBLY

Open Assembly Time should be kept as short as possible, particularly under hot and dry conditions. Over-dried glued veneer results in poor wetting of the opposite veneer, which results in weak bonding.

8. CLEANING

The equipment like glue mixer, spreader should be cleaned with warm water and this should be done before the glue is completely cured.

10. PACKING

25 Kg packing available in HDP/PP bag with polyethylene liner.

12. STORAGE

Store in original bags in a cool and dry place to protect from heat and moisture. The resin is hygroscopic in nature, so it should be stored in moisture free area. The limitation of the resin is the viscosity which will increase with time. Also the rate of increase of viscosity is dependent on storage temperature. Shelf Life at 20 – 25 ° C is 6 months.

3. GLUE MAKING PROCEDURE

Take 50% of the total water in glue mixer. Add resin powder and required quantity of wheat our and CSP. Mix well for 15-20 minutes until all powder dissolved and lump free paste is prepared. Then add rest of water and mix well for 10 minutes. Temperature may be maintained 20-35°C.

After addition of all ingredients and subsequent mixing, check viscosity, if needed some water may be added to maintain the required viscosity 14-18seconds in B6 cup.

5. GLUE CONSUMPTION

The veneer surface should be properly cleaned and free from dust and other contamination. Veneer should be at with uniform thickness. The moisture content of the veneers should be within the range of 6-8%. Higher moisture content increases the risk of blisters and bleedthrough, whereas over dried veneers may cause poor face bonding and starved joints. In general, the consumption of glue varies between 300 to 450 Gms per square meter based on manufacturing condition and veneer quality.

7. HOT PRESSING CONDITION

Hot pressing time and pressure varies for different wood density. Normally wood density varies from than 500 – 600 kg/cubic meter.

For wood density less than 550 kg/cubic meter, Hot Press pressure 8-12 Kg/sq.cm and for wood density more than 550 kg/cubic meter, Hot Press pressure 14-16 kg/sq.cm

Hot press temperature to be maintained between 140 to 150°C depending on the thickness of veneer and Hot Press pressure.

Hot pressing time = Basic setting time at 135°C (3.5 minutes) (equivalent to gel time) + Heat transfer time to the farthest glue line (normally 0.8 to 1 minute per mm; such as for 6 mm thickness, farthest glue line is 3 mm, so heat transfer time to the farthest glue line is 2.4 to 3 minute.) Since the rate of heat transfer is dependent on the wood species and the moisture content, the above information can only serve as a guide.

9. MAJOR APPLICATION AREAS

Glue for the manufacture of BWP grade plywood, Block Board and to prepare boards which are to be used in highly humid area.

Glue for the exterior application

11. HANDLING

WINDBOND PF-101P contains small amount of Formaldehyde. Hence, direct skin contact with the resin should be avoided. There should be enough ventilation in work areas for glue preparation and pressing is done.